物理性质
|
|
比重
|
ASTM D792
|
Natural 或代表 color
|
-
|
1.26
|
|
熔融指数
|
ASTM D1238
|
220℃, 10kg
|
g/10min
|
22
|
|
熔融指数
|
ASTM D1238
|
250℃, 2.16kg
|
g/10min
|
7
|
|
成型收缩率(MD)
|
ASTM D955
|
Flow at 3.2mm(MD)
|
%
|
0.2-0.5
|
|
成型收缩率(TD)
|
ASTM D955
|
X-Flow at 3.2mm(TD)
|
%
|
0.2-0.5
|
|
ASH content
|
ASTM D5630
|
-
|
%
|
9.5
|
|
机械性质
|
|
拉伸强度(at yield)
|
ASTM D638
|
5mm/min
|
kgf/cm2
|
600
|
|
伸长率(at break)
|
ASTM D638
|
5mm/min
|
%
|
4
|
|
拉伸模量35000
|
ASTM D638
|
5mm/min
|
kgf/cm2
|
35000
|
|
断裂强度(at break)
|
ASTM D638
|
5mm/min
|
kgf/cm2
|
600
|
|
弯曲强度
|
ASTM D790
|
2.8mm/min
|
kgf/cm2
|
980
|
|
弯曲模量
|
ASTM D790
|
2.8mm/min
|
kgf/cm2
|
40000
|
|
Izod冲击强度(notched)
|
ASTM D256
|
1/4 inch at 23°C
|
kgf·cm/cm
|
8
|
|
Izod冲击强度(notched)
|
ASTM D256
|
1/8 inch at 23°C
|
kgf·cm/cm
|
8
|
|
硬度
|
ASTM D785
|
R-Scale
|
-
|
118
|
|
热学特性
|
|
热变形温度
|
ASTM D648
|
18.56kgf/cm2, 6.4mm
|
°C
|
96
|
|
热变形温度
|
ASTM D648
|
4.6kgf/cm2, 6.4mm
|
°C
|
97
|
|
维卡软化温度
|
ISO 306
|
B/50
|
°C
|
99
|
|
Tg
|
DSC
|
-
|
°C
|
101
|
|
阻燃
|
|
阻燃度
|
UL94
|
V-0
|
mm
|
2.0, 3.0
|
...