Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
670
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
710
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
7
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
>50
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
21400
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
960
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
22400
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
65
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
60
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
6
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
85
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2150
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
100
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2300
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, unnotched, 23°C
|
NB
|
cm-kgf/cm
|
ASTM D 4812
|
|
|
Izod Impact, notched, 23°C
|
61
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
1223
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, unnotched 80*10*3 -30°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, notched 80*10*3 +23°C
|
53
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*3 -30°C
|
11
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
54
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
|
13
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
166
|
°C
|
ASTM D 1525
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
148
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
142
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
8.E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
8.E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, flow
|
8.E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, -40°C to 40°C, xflow
|
8.E-05
|
1/°C
|
ISO 11359-2
|
|
|
Ball Pressure Test, 125°C +/- 2°C
|
pass
|
-
|
IEC 60695-10-2
|
|
|
Vicat Softening Temp, Rate B/50
|
155
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
157
|
°C
|
ISO 306
|
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
149
|
°C
|
ISO 75/Be
|
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
137
|
°C
|
ISO 75/Ae
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.2
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage on Tensile Bar, flow (2)
|
0.6 - 0.8
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, flow, 3.2 mm
|
0.6 - 0.8
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm
|
0 - 0.2
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
6
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.2
|
g/cm2
|
ISO 1183
|
|
|
Water Absorption, (23°C/sat)
|
0.16
|
%
|
ISO 62
|
|
|
Moisture Absorption (23°C / 50% RH)
|
0.35
|
%
|
ISO 62
|
|
|
Melt Volume Rate, MVR at 300°C/1.2 kg
|
6
|
cm210 min
|
ISO 1133
|
|
|
Melt Volume Rate, MVR at 330°C/2.16kg
|
29
|
cm210 min
|
ISO 1133
|
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
120
|
°C
|
|
Drying Time
|
2 - 4
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
290 - 320
|
°C
|
|
Nozzle Temperature
|
280 - 310
|
°C
|
|
Front - Zone 3 Temperature
|
290 - 320
|
°C
|
|
Middle - Zone 2 Temperature
|
280 - 310
|
°C
|
|
Rear - Zone 1 Temperature
|
270 - 300
|
°C
|
|
Hopper Temperature
|
60 - 80
|
°C
|
|
Mold Temperature
|
80 - 120
|
°C
|